Research Article
In Vitro Evaluation of Some Types of Ferrimagnetic Glass Ceramics
| Sample | Time/weeks | Si | Ca | P | Fe |
| Mg | 1 | 0.129 | 44.74 | 2.08 | — | 2 | — | 0.310 | 0.032 | 0.21 | 4 | 1.080 | 103.99 | 0.014 | 0.01 |
| Ca | 1 | 0.137 | 48.430 | 2.05 | — | 2 | — | 45.97 | 0.023 | 0.03 | 4 | 0.010 | 60.64 | 0.07 | 0.08 |
| Mn | 1 | 0.131 | 49.66 | 2.88 | — | 2 | — | 57.54 | 3.455 | 0.11 | 4 | 0.770 | — | 0.66 | 0.02 |
| Cu | 1 | 0.157 | 56.52 | 6.08 | — | 2 | — | 35.93 | 0.015 | 0.09 | 4 | 0.610 | 89.31 | 0.002 | 0.05 |
| Zn | 1 | 0.124 | 54.16 | 2.17 | — | 2 | — | 33.65 | 1.68 | 0.01 | 4 | 3.310 | 51.621 | 0.010 | 0.02 |
| Ce | 1 | 0.322 | 45.02 | 1.39 | — | 2 | — | 66.40 | 4.76 | 2.29 | 4 | 0.120 | 78.03 | 0.09 | 0.04 |
|
|