Toughening of Poly(L-lactide) with Blends of Poly(
-caprolactone-
co
-L-lactide) in the Presence of Chain Extender
Table 3
Mechanical properties of PLLA/copolyester blends.
PLLA/copolyester ratio (w/w)
Joncryl® content (phr)
Young’s modulus (MPa)
Stress at break (MPa)
Elongation at break (%)
Impact strength (kJ/m
2
)
Hardness Shore D
60/40
-
209 ± 58
10.9 ± 1.9
57.3 ± 8.2
4.3 ± 0.8
54.3 ± 1.2
60/40
1.0
240 ± 69
11.2 ± 2.2
40.0 ± 1.8
14.5 ± 0.6
57.4 ± 0.7
60/40
2.0
328 ± 16
14.6 ± 1.2
15.8 ± 6.0
16.9 ± 1.4
58.5 ± 0.9
100/0
2.0
1491 ± 38
57.6 ± 2.3
6.0 ± 0.3
2.2 ± 0.5
87.2 ± 0.8
90/10
2.0
1210 ± 101
44.8 ± 2.0
6.2 ± 0.2
3.3 ± 0.6
81.2 ± 1.8
80/20
2.0
1122 ± 46
41.8 ± 0.2
6.1 ± 0.1
5.6 ± 0.9
66.7 ± 0.8