Influence of Breast Implant Surface Finishing on Physicochemical and Mechanical Properties before and after Extreme Degradation Studies
Table 5
Tukey’s test results from comparison of degradation process over mechanical properties.
| Property | Comparison of degradation group process | value |
| Mechanical strength (MPa) at 450% strain | Basic-acid | 0.012 | As received-acid | 0.076 | As received-basic | 0.668 |
| Mechanical strength (MPa) at rupture | Basic-acid | 0.011 | As received-acid | 0.882 | As received-basic | 0.004 |
| Deformation (%) at rupture | Basic-acid | 0.195 | As received-Acid | 0.048 | As received-basic | <0.001 |
|
|