UAE Neem Extract as a Corrosion Inhibitor for Carbon Steel in HCl Solution
Table 4
The data obtained from the weight loss measurements for Arrhenius Equation: (
/
) against Ln (Corrosion Rate).
| | Ln (Corrosion Rate)/mgcm−2h−1 | (1/) 103/K−1 | 1.0 M HCl | 1.0 M HCl+ 0.02 g/L | 1.0M HCl+ 0.20 g/L | 1.0 M HCl+ 0.50 g/L | 1.0 M HCl+ 1.00 g/L | 1.0 M HCl+ 2.00 g/L |
| 3.30 | −0.03978 | −0.60148 | −1.09064 | −1.38629 | −1.50959 | −1.65026 | 3.19 | 0.33218 | −0.08338 | −0.51083 | −0.59059 | −0.66165 | −0.80744 | 3.10 | 1.54137 | 1.29281 | 1.09494 | 0.86794 | 0.72028 | 0.59993 | 3.00 | 2.50348 | 2.4201 | 2.39817 | 2.21583 | 2.07493 | 1.99266 | 2.92 | 3.26881 | 3.47581 | 3.43431 | 3.3176 | 3.22799 | 3.18544 |
|
|