Effect of Magnesium Hydride on the Corrosion Behavior of Pure Magnesium in 0.1 M NaCl Solution

<table>Comparison of Raman spectra for the pure magnesium polarized in 0.1 M NaCl solution for 30 minutes (a) <svg height="4.8874998" id="M28" style="vertical-align:-0.0pt" version="1.1" viewbox="0 0 10.1 4.8874998" width="10.1" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink">
<g transform="matrix(.017,-0,0,-.017,.062,4.825)"><path d="M535 230h-483v50h483v-50z" id="x2212"></path></g>
</svg>2.0 V/SCE (b) <svg height="4.8874998" id="M29" style="vertical-align:-0.0pt" version="1.1" viewbox="0 0 10.1 4.8874998" width="10.1" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink">
<g transform="matrix(.017,-0,0,-.017,.062,4.825)"><path d="M535 230h-483v50h483v-50z" id="x2212"></path></g>
</svg>0.8 V/SCE.</table>

International Journal of Corrosion

fig5

Figure 5

Figure 5: Effect of Magnesium Hydride on the Corrosion Behavior of Pure Magnesium in 0.1 M NaCl Solution 