Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions
Table 2
Temperature-dependent results of samples machined parallel to the rolling direction.
| Sample | Temperature | Total pressure | | | | Elongation | | Reductionin area | | (°C) | (kPa) | (mm) | (mm) | (mm) | (%) | (mm) | (%) |
| L1 | 20 | 350 | 10.3 | 23.7 | 34.0 | 17.8 | 3.05 | 41.8 | L3 | 20 | 500 | 23.8 | 10.35 | 34.15 | 18.4 | 3.20 | 36.0 | L15 | 20 | 800 | 14.1 | 20.3 | 34.4 | 19.6 | 3.30 | 31.9 | L13 | 20 | 1000 | 23.6 | 10.1 | 33.7 | 16.4 | 3.55 | 21.2 | L10 | 20 | Air | 11.0 | 25.5 | 36.5 | 28.9 | 2.20 | 69.8 | L16 | 30 | 800 | 11.2 | 22.8 | 34.0 | 17.8 | 3.35 | 30.3 | L7 | 35 | 800 | 10.2 | 22.1 | 32.3 | 10.2 | 3.68 | 15.6 | L4 | 35 | 800 | 12.5 | 21.4 | 33.9 | 17.3 | 3.30 | 31.9 | L9 | 40 | 200 | 23.2 | 11.7 | 34.9 | 21.8 | 3.00 | 43.8 | L6 | 40 | 800 | 11.1 | 22.15 | 33.25 | 14.4 | 3.45 | 25.6 | L8 | 45 | 800 | 23.2 | 10.2 | 33.4 | 15.1 | 3.55 | 21.2 | L14 | 50 | 800 | 20.5 | 12.5 | 32.0 | 13.5 | 3.45 | 25.6 | L17 | 60 | 800 | 24.7 | 8.5 | 33.2 | 14.4 | 3.35 | 29.4 |
|
|
*This total length includes the shoulders of the specimen and does not refer to the gauge length.
|