Hot Corrosion Behavior of High-Chromium, High-Carbon Cast Irons in NaCl-KCl Molten Salts
Table 1
Chemical composition of castings (wt.%).
| Alloy | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 304SS |
| C | 5.17 | 5.09 | 4.65 | 4.29 | 4.1 | 3.93 | 3.93 | 0.08 | Mn | 6.27 | 5.1 | 4.8 | 5.9 | 5.6 | 7.42 | 6.5 | 2 | Si | 0.34 | 0.32 | 0.32 | 0.42 | 0.4 | 0.32 | 0.28 | 1 | S | 0.02 | 0.02 | 0.02 | 0.01 | 0.02 | 0.02 | 0.01 | 0.03 | P | 0.15 | 0.05 | 0.05 | 0.05 | 0.05 | 0.05 | 0.17 | 0.045 | Cr | 21 | 21.2 | 22.52 | 30.48 | 29.7 | 27.7 | 28.7 | 19 | Ni | 1.58 | 1.8 | 1.68 | 1.96 | 1.94 | 1.86 | 1.81 | 9.5 | Mo | 2.2 | 0.92 | 2.47 | 3.3 | 3.25 | 0.98 | 1.04 | — | V | 0.85 | 0.87 | 0.615 | 0.53 | 1.16 | 1.14 | 0.57 | — | Ti | 0.23 | 0.24 | 0.11 | 0.06 | 0.21 | 0.13 | 0.05 | — | CE | 5.31 | 5.21 | 4.77 | 4.45 | 4.27 | 4.06 | 3.97 | 0.42 | CrE | 23.04 | 27.63 | 29.94 | 38.95 | 41.3 | 35.53 | 33.76 | 20.5 |
|
|