Volume 2013, Article ID 453835, 9 pages
http://dx.doi.org/10.1155/2013/453835
Research Article

Electrochemical and Oxidation Behavior of Yttria Stabilized Zirconia Coating on Zircaloy-4 Synthesized via Sol-Gel Process

1Department of Technical Inspection Engineering, Petroleum University of Technology (PUT), Abadan Institute of Technology (AIT), P.O. Box 619, Abadan 6318714331, Iran
2Department of Material Science Engineering, Isfahan University of Technology (IUT), Isfahan 8415683111, Iran

Received 24 April 2013; Revised 23 November 2013; Accepted 25 November 2013

Academic Editor: W. Ke

Copyright © 2013 S. Rezaee et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. Y. Chen, M. Urquidi-Macdonald, and D. D. Macdonald, “The electrochemistry of zirconium in aqueous solutions at elevated temperatures and pressures,” Journal of Nuclear Materials, vol. 348, no. 1-2, pp. 133–147, 2006. View at Publisher · View at Google Scholar · View at Scopus
  2. D. W. Shoesmith and D. Zagidulin, “The corrosion of zirconium under deep geologic repository conditions,” Journal of Nuclear Materials, vol. 418, no. 1–3, pp. 292–306, 2011. View at Publisher · View at Google Scholar · View at Scopus
  3. D. Q. Peng, X. D. Bai, X. W. Chen et al., “Corrosion behavior of tin ions implanted zirconium in 1N H2SO4,” Applied Surface Science, vol. 239, no. 3-4, pp. 342–352, 2005. View at Publisher · View at Google Scholar · View at Scopus
  4. D. Q. Peng, X. D. Bai, X. W. Chen, Q. G. Zhou, X. Y. Liu, and P. Y. Deng, “Comparison of aqueous corrosion behavior of zirconium and zircaloy-4 implanted with molybdenum,” Nuclear Instruments and Methods in Physics Research B, vol. 211, no. 1, pp. 55–68, 2003. View at Publisher · View at Google Scholar · View at Scopus
  5. L. Cadoret, N. Reuge, S. Pannala et al., “Silicon chemical vapor deposition on macro and submicron powders in a fluidized bed,” Powder Technology, vol. 190, no. 1-2, pp. 185–191, 2009. View at Publisher · View at Google Scholar · View at Scopus
  6. M. Brunet, H. M. Kotb, L. Bouscayrol et al., “Nanocrystallized tetragonal metastable ZrO2 thin films deposited by metal-organic chemical vapor deposition for 3D capacitors,” Thin Solid Films, vol. 519, no. 16, pp. 5638–5644, 2011. View at Publisher · View at Google Scholar · View at Scopus
  7. C. Giolli, F. Borgioli, A. Credi et al., “Characterization of TiO2 coatings prepared by a modified electric arc-physical vapour deposition system,” Surface and Coatings Technology, vol. 202, no. 1, pp. 13–22, 2007. View at Publisher · View at Google Scholar · View at Scopus
  8. W. Xue, Q. Zhu, Q. Jin, and M. Hua, “Characterization of ceramic coatings fabricated on zirconium alloy by plasma electrolytic oxidation in silicate electrolyte,” Materials Chemistry and Physics, vol. 120, no. 2-3, pp. 656–660, 2010. View at Publisher · View at Google Scholar · View at Scopus
  9. D. Q. Peng, X. D. Bai, and B. S. Chen, “Surface analysis and corrosion behavior of zirconium samples implanted with yttrium and lanthanum,” Surface and Coatings Technology, vol. 190, no. 2-3, pp. 440–447, 2005. View at Publisher · View at Google Scholar · View at Scopus
  10. D. Q. Peng, X. D. Bai, X. W. Chen, Q. G. Zhou, X. Y. Liu, and R. H. Yu, “Corrosion behavior in 1 N H2SO4 of zirconium ion implanted with nickel,” Surface and Coatings Technology, vol. 187, no. 2-3, pp. 300–306, 2004. View at Publisher · View at Google Scholar · View at Scopus
  11. P. Kiruthika, R. Subasri, A. Jyothirmayi, K. Sarvani, and N. Y. Hebalkar, “Effect of plasma surface treatment on mechanical and corrosion protection properties of UV-curable sol-gel based GPTS-ZrO2 coatings on mild steel,” Surface and Coatings Technology, vol. 204, no. 8, pp. 1270–1276, 2010. View at Publisher · View at Google Scholar · View at Scopus
  12. W. Liu, Y. Chen, C. Ye, and P. Zhang, “Preparation and characterization of doped sol-gel zirconia films,” Ceramics International, vol. 28, no. 4, pp. 349–354, 2002. View at Publisher · View at Google Scholar · View at Scopus
  13. A. Díaz-Parralejo, A. Macías-García, J. Sánchez-González, M. Á. Díaz-Díez, and E. M. Cuerda-Correa, “Influence of the experimental parameters on the synthesis process of yttria-doped zirconia sol-gel films,” Surface and Coatings Technology, vol. 204, no. 14, pp. 2257–2261, 2010. View at Publisher · View at Google Scholar · View at Scopus
  14. M. A. D. Crespo, A. G. Murillo, A. M. Torres-Huerta, C. Yañez-Zamora., and F. D. J. Carrillo-Romo, “Electrochemical behaviour of ceramic yttria stabilized zirconia on carbon steel synthesized via sol-gel process,” Journal of Alloys and Compounds, vol. 483, no. 1-2, pp. 437–441, 2009. View at Publisher · View at Google Scholar · View at Scopus
  15. A. J. López, J. Rams, and A. Ureña, “Sol-gel coatings of low sintering temperature for corrosion protection of ZE41 magnesium alloy,” Surface and Coatings Technology, vol. 205, no. 17-18, pp. 4183–4191, 2011. View at Publisher · View at Google Scholar · View at Scopus
  16. N. N. Voevodin, N. T. Grebasch, W. S. Soto et al., “An organically modified zirconate film as a corrosion-resistant treatment for aluminum 2024-T3,” Progress in Organic Coatings, vol. 41, no. 4, pp. 287–293, 2001. View at Publisher · View at Google Scholar · View at Scopus
  17. L. Paussa, N. C. Rosero Navarro, D. Bravin et al., “ZrO2 sol-gel pre-treatments doped with cerium nitrate for the corrosion protection of AA6060,” Progress in Organic Coatings, vol. 74, no. 2, pp. 311–319, 2012. View at Publisher · View at Google Scholar · View at Scopus
  18. M. Jokinen, M. Patsi, H. Rahiala, T. Peltola, M. Ritala, and J. B. Rosenholm, “Influence of sol and surface properties on in vitro bioactivity of sol-gel-derived TiO2 and TiO2-SiO2 films deposited by dip-coating method,” Journal of Biomedical Materials Research A, vol. 42, no. 2, pp. 295–302, 1998. View at Publisher · View at Google Scholar
  19. M. A. Domínguez-Crespo, A. García-Murillo, A. M. Torres-Huerta, F. J. Carrillo-Romo, E. Onofre-Bustamante, and C. Yáñez-Zamora, “Characterization of ceramic sol-gel coatings as an alternative chemical conversion treatment on commercial carbon steel,” Electrochimica Acta, vol. 54, no. 10, pp. 2932–2940, 2009. View at Publisher · View at Google Scholar · View at Scopus
  20. Q. Li, X. Zhong, J. Hu, and W. Kang, “Preparation and corrosion resistance studies of zirconia coating on fluorinated AZ91D magnesium alloy,” Progress in Organic Coatings, vol. 63, no. 2, pp. 222–227, 2008. View at Publisher · View at Google Scholar · View at Scopus
  21. Y. S. Baron and A. Ruiz, “Sol-gel coating to reduce 1.25 Cr-0.5 Mo steel oxidation at 700°C: catalyst type effect,” Corrosion Science, vol. 53, no. 3, pp. 1060–1065, 2011. View at Publisher · View at Google Scholar · View at Scopus
  22. R. Ugas-Carrión, F. Sittner, C. J. Ochs, S. Flege, and W. Ensinger, “Characterization of the porosity of thin zirconium oxide coatings prepared at low temperatures,” Thin Solid Films, vol. 517, no. 6, pp. 1967–1969, 2009. View at Publisher · View at Google Scholar · View at Scopus
  23. E. Nouri, M. Shahmiri, H. R. Rezaie, and F. Talayian, “A comparative study of heat treatment temperature influence on the thickness of zirconia sol-gel thin films by three different techniques: SWE, SEM and AFM,” Surface and Coatings Technology, vol. 206, no. 19-20, pp. 3809–3815, 2012. View at Publisher · View at Google Scholar · View at Scopus
  24. P. C. R. Varma, B. Duffy, and J. Cassidy, “Influence of magnesium nitrate on the corrosion performance of sol-gel coated AA2024-T3 aluminium alloy,” Surface and Coatings Technology, vol. 204, no. 3, pp. 277–284, 2009. View at Publisher · View at Google Scholar · View at Scopus
  25. M. G. Fontana, Corrosion Engineering, McGraw-Hill, Singapore, 1986.
  26. S. K. Tiwari, J. Adhikary, T. B. Singh, and R. Singh, “Preparation and characterization of sol-gel derived yttria doped zirconia coatings on AISI 316L,” Thin Solid Films, vol. 517, no. 16, pp. 4502–4508, 2009. View at Publisher · View at Google Scholar · View at Scopus
  27. M. T. Soo, N. Prastomo, A. Matsuda et al., “Elaboration and characterization of sol-gel derived ZrO2 thin films treated with hot water,” Applied Surface Science, vol. 258, no. 13, pp. 5250–5258, 2012. View at Publisher · View at Google Scholar · View at Scopus
  28. E. Nouri, M. Shahmiri, H. R. Rezaie, and F. Talayian, “Investigation of structural evolution and electrochemical behaviour of zirconia thin films on the 316L stainless steel substrate formed via sol-gel process,” Surface and Coatings Technology, vol. 205, no. 21-22, pp. 5109–5115, 2011. View at Publisher · View at Google Scholar · View at Scopus
  29. Q. Li, B. Chen, S. Xu, H. Gao, L. Zhang, and C. Liu, “Structural and electrochemical behavior of sol-gel ZrO2 ceramic film on chemically pre-treated AZ91D magnesium alloy,” Journal of Alloys and Compounds, vol. 478, no. 1-2, pp. 544–549, 2009. View at Publisher · View at Google Scholar · View at Scopus
  30. A. E. Markowitz, Optimization of sol-gel composite films through chemical and thermal processing [M.S. thesis], Queen’s University, Ontario, Canada, 1998.
  31. H. Kozuka and M. Kajimura, “Single-step dip coating of crack-free BaTiO3 films > 1 μm thick: effect of poly (vinylpyrrolidone) on critical thickness,” Journal of the American Ceramic Society, vol. 83, no. 5, pp. 1056–1062, 2000. View at Publisher · View at Google Scholar · View at Scopus
  32. H. Li, K. Liang, L. Mei, S. Gu, and S. Wang, “Oxidation protection of mild steel by zirconia sol-gel coatings,” Materials Letters, vol. 51, no. 4, pp. 320–324, 2001. View at Publisher · View at Google Scholar · View at Scopus