Monitoring the Interaction of Two Heterocyclic Compounds on Carbon Steel by Electrochemical Polarization, Noise, and Quantum Chemical Studies
Table 2
Potentiodynamic polarization parameters of CS in the presence and absence of P2APH and RP2APH in 1 M HCl at
°C for immersion period of 30 min.
| | P2APH | RP2APH | (mM) | (mV/SCE) | (μA/cm2) | (mV/dec) | (mV/dec) | | − (mV/SCE) | (μA/cm2) | (mV/dec) | (mV/dec) | |
| 0 | 531 | 639.31 | 102 | 152 | — | 531 | 639.31 | 102 | 152 | | 0.2 | 511 | 383.20 | 110 | 137 | 40.03 | 433 | 375.61 | 126 | 161 | 41.22 | 0.4 | 497 | 219.93 | 85 | 123 | 66.68 | 517 | 249.71 | 122 | 175 | 60.92 | 0.6 | 488 | 108.08 | 67 | 126 | 83.08 | 511 | 206.93 | 94 | 162 | 67.62 | 0.8 | 501 | 55.67 | 52 | 126 | 91.23 | 509 | 105.76 | 119 | 168 | 83.45 | 1.0 | 484 | 49.40 | 112 | 136 | 92.27 | 512 | 77.55 | 146 | 167 | 87.86 |
|
|