International Journal of Corrosion / 2016 / Article / Tab 2 / Research Article
Study of New Thiazole Based Pyridine Derivatives as Potential Corrosion Inhibitors for Mild Steel: Theoretical and Experimental Approach Table 2 Corrosion rate and inhibition efficiency for weight loss measurement in the absence and presence of inhibitors in 0.5 M HCl at different concentrations and temperatures.
Inhibitor (mM) 30°C % IE 40°C % IE 50°C % IE 60°C % IE (mg cm2 h−1 ) (mg cm−2 h−1 ) (mg cm2 h−1 ) (mg cm−2 h−1 )Blank — 0.516 — 0.883 — 1.224 — 1.65 — 2-MTPH 0.22 0.171 66.8 ± 0.78 0.316 64.2 ± 1.12 0.467 61.8 ± 0.55 0.6554 60.2 ± 0.38 0.44 0.122 76.3 ± 0.44 0.2296 73.9 ± 0.96 0.364 70.2 ± 0.38 0.528 68 ± 0.4 0.66 0.0598 88.41 ± 1.2 0.1348 84.7 ± 0.87 0.2678 78.1 ± 0.46 0.4224 74.4 ± 0.84 0.88 0.0198 96.16 ± 1.14 0.087 90.1 ± 0.62 0.2112 82.7 ± 1.32 0.346 79 ± 0.52 3-MTPH 0.22 0.2542 50.73 ± 0.96 0.4654 47.29 ± 0.45 0.6762 44.7 ± 1.05 0.9898 40 ± 0.63 0.44 0.1736 66.35 ± 0.88 0.3476 60.63 ± 0.84 0.53 56.6 ± 0.81 0.7984 51.6 ± 1.06 0.66 0.1124 78.21 ± 0.39 0.2206 75.01 ± 0.76 0.4112 66.4 ± 0.92 0.6598 60 ± 0.74 0.88 0.0738 85.6 ± 0.47 0.183 79.27 ± 0.56 0.3092 74.7 ± 0.38 0.5588 66.1 ± 0.46 4-MTPH 0.22 0.2492 51.70 ± 1.08 0.44 50.16 ± 0.83 0.6728 45 ± 0.50 0.95 42.4 ± 0.54 0.44 0.1698 67.09 ± 0.26 0.3142 64.41 ± 0.88 0.4728 61.3 ± 0.44 0.7258 56.0 ± 0.58 0.66 0.107 79.26 ± 0.38 0.2382 73.02 ± 0.74 0.4024 67.1 ± 0.68 0.6242 62.1 ± 0.68 0.88 0.069 86.6 ± 0.44 0.165 81.31 ± 0.32 0.3164 74.1 ± 0.54 0.5056 69.3 ± 0.78