Research Article
Effect of Grain Size on the Stress Corrosion Cracking of Ultrafine Grained Cu-10 wt% Zn Alloy in Ammonia
Table 1
Processing recipes and grain size.
| Sample | Deformation | Annealing | Grain size (μm) |
| 1 | None | None | 38.0 | 2 | CR 50% | 673 K-60 min | 12.6 | 3 | CR 50% | 623 K-60 min | 3.30 | 4 | ECAP 2 pass | 623 K-15 min | 1.10 | 5 | ECAP 2 pass | 623 K-10 min | 0.71 | 6 | ECAP 2 pass | 623 K-5 min | 0.44 | 7 | ECAP 8 pass | 473 K-10 min | 0.15 | 8 | ECAP 8 pass | 473 K-1 min | 0.12 | 9 | ECAP 8 pass | | 0.12 |
|
|