Research Article
Experimental Study on the Influence of Sulfate Reducing Bacteria on the Metallic Corrosion Behavior under Disbonded Coating
Table 2
The electrochemical parameters.
| Simulated solution | Experiment time | Stripping depths/mm | The corrosion current density/A/cm2 | The self-corrosion potential/mV | The ratio of anode Tafel slope and cathode Tafel slope |
| Soil simulated solution (No. 1) | 1 d | 0 | 23.1029 | −702 | 1.7328 | 80 | 19.2514 | −722 | 1.6538 | 160 | 11.5943 | −718 | 1.5963 | 7 d | 0 | 43.7829 | −708 | 1.5726 | 80 | 30.3086 | −722 | 1.5250 | 160 | 26.0457 | −725 | 1.4844 | 14 d | 0 | 45.2457 | −701 | 1.4111 | 80 | 32.3429 | −717 | 1.4049 | 160 | 27.7543 | −723 | 1.4831 |
| Soil simulated solution + SRB (No. 2) | 1 d | 0 | 25.8171 | −688 | 1.8134 | 80 | 20.2457 | −696 | 1.6897 | 160 | 19.5143 | −700 | 1.6727 | 7 d | 0 | 30.9143 | −688 | 1.7509 | 80 | 28.4971 | −692 | 1.7250 | 160 | 21.7143 | −695 | 1.6395 | 14 d | 0 | 78.5143 | −675 | 1.7515 | 80 | 87.6457 | −680 | 1.2216 | 160 | 95.4914 | −676 | 1.0870 |
| Soil simulated solution + SRB + fungicide (No. 3) | 1 d | 0 | 16.3886 | −694 | 1.9859 | 80 | 19.0400 | −692 | 1.4779 | 160 | 21.2457 | −696 | 1.3274 | 7 d | 0 | 32.4343 | −698 | 1.6243 | 80 | 40.1143 | −732 | 1.4063 | 160 | 43.4286 | −691 | 1.4588 | 14 d | 0 | 45.6114 | −684 | 1.4157 | 80 | 58.8800 | −689 | 1.4475 | 160 | 64.1714 | −684 | 1.4206 |
|
|