Wet Oxidation Behavior of Near-Stoichiometric SiC Fibres in the Simulated Aeroengine Circumstance

Figure 2

The oxygen content and oxide layer thickness of KD-S fibres after annealing at 1000-1500°C for 1 h. (a) Oxygen content and (b) oxide layer thickness.

(a)

(b)