Hot Corrosion of SrTiO3 Perovskite in Na2SO4 + 50 wt.% V2O5 and Na2SO4 + 10 wt.% NaCl Environments at 900°C
Figure 3
(a) Lower magnification image of SrTiO3 sample before exposure to hot corrosion and (b) higher magnification image of (a). EDX analysis was done on the surface of (b) at region 1 (corresponding to SrTiO3).