Hot Corrosion of SrTiO₃ Perovskite in Na₂SO₄ + 50 wt.% V₂O₅ and Na₂SO₄ + 10 wt.% NaCl Environments at 900°C

Table 1

The elemental compositions of SrTiO₃ samples before and after being subjected to hot corrosion in both Na₂SO₄ + 50 wt.% V₂O₅ and Na₂SO₄ + 10 wt.% NaCl environments at 900°C.

S. No	Figures	Environments	Regions	Elements (wt.%)
				O	Ti	V	Sr
1	Figure 3(b)	Before hot corrosion	1	24.80	22.82	-	52.38
2	Figure 4(b)	Na2SO4 + 50 wt.% V2O5	1	24.94	23.14	-	51.92
3	Figure 4(c)	Na2SO4 + 50 wt.% V2O5	1	25.03	-	18.83	56.14
4	Figure 6(b)	Na2SO4 + 10 wt.% NaCl	1	26.90	27.92	-	45.18