Microstructure and Damping Capacity of ZK60 Alloy Sheets Fabricated by Twin Roll Casting and Hot Rolling Process
Table 2
Mechanical properties and damping capacity of the sheets after T6 treatment.
| Reduction ratio per pass | Mechanical properties | Damping capacity | UT.S. | Y.S. | EL. | | |
| 10% | 414±4 MPa | 315±13 MPa | 17.6 ±3.5 % | 0.00702 | 0.01816 | 30% | 430±13 MPa | 301±19 MPa | 18.3 ±3.2 % | 0.00522 | 0.01734 | 50% | 382±15 MPa | 281±20 MPa | 17.8 ±2.6 % | 0.00425 | 0.01759 |
|
|