Effect of Alternating Stray Current Density on Corrosion Behavior of X80 Steel under Disbonded Coating

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="6"><hr/></td></tr><tr class="thead"><td class="align_left">Ingredient</td><td class="align_center">H<sub>2</sub>O</td><td class="align_center">Na<sub>2</sub>CO<sub>3</sub></td><td class="align_center">NaCl</td><td class="align_center">Na<sub>2</sub>SO<sub>4</sub></td><td class="align_center">NaHCO<sub>3</sub></td></tr><tr><td class="thead-hr" colspan="6"><hr/></td></tr><tr><td class="align_left">Content</td><td class="align_center">1000 mL</td><td class="align_center">0.1600 g</td><td class="align_center">0.5125 g</td><td class="align_center">0.1712 g</td><td class="align_center">0.0865 g</td></tr><tr class="table-tr"><td colspan="6"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Composition of soil simulated solution.</div>

International Journal of Corrosion

tab2

Table 2

Table 2: Effect of Alternating Stray Current Density on Corrosion Behavior of X80 Steel under Disbonded Coating 