International Journal of Corrosion / 2022 / Article / Tab 6 / Research Article
Electrochemical, Isotherm, and Material Strength Studies of Cucumeropsis mannii Shell Extract on A515 Grade 70 Carbon Steel in NaCl Solution Table 6 Batch experimental results showing CMSE influence on corrosion rate, yield strength, Young modulus, and hardness of carbon steel in 1.0 M NaCl at different temperature, time, and load.
Run (°C) (day) (g L-1 )Corrosion rate (mm/y) Load ( ) Young modulus (GPa) Hardness (BHN) With CMSE Without CMSE With CMSE Without CMSE With CMSE Without CMSE 1 30 1 10 0.096 0.306 30000 198.9 187.8 104.1 99 2 60 1 10 0.36 1.211 15000 196.4 189.1 97.2 93.4 3 30 5 10 0.125 0.475 15000 198.7 188.6 106.4 101.6 4 60 5 10 0.516 1.348 30000 180.9 171.7 89.4 86.4 5 45 3 6 0.329 1.587 22500 186.4 178.1 96.1 92.1 6 45 3 6 0.306 0.818 7500 199.5 194.2 100.8 97 7 45 3 14 0.216 0.648 22500 187.4 183.7 99.6 95.7 8 30 5 2 0.197 0.591 15000 193.1 183.2 102.3 97.6 9 30 5 10 0.139 0.417 30000 191.3 183.9 98.7 93.7 10 45 3 2 0.37 1.019 22500 182.6 176.9 95.5 91 11 45 3 6 0.285 0.955 22500 185.6 178.1 98.5 93.8 12 45 3 6 0.351 1.153 37500 179.6 174.4 93.8 89.6 13 45 3 6 0.333 0.882 22500 191.1 178.1 95.8 91.8 14 45 3 6 0.296 0.888 22500 184.8 178.1 97.2 92.6 15 45 3 6 0.309 0.927 22500 183.1 178.1 96.7 92.1 16 15 3 6 0.131 0.593 22500 197.3 194.2 103.8 100.4 17 30 1 10 0.0728 0.218 15000 202.4 194.8 112.3 107.2 18 45 1 6 0.241 0.923 22500 188.2 181.7 97.7 94.3 19 60 1 2 0.604 1.812 30000 176.7 170.4 88.8 86 20 75 3 6 0.388 1.164 22500 181.2 173.8 94.3 91.5 21 30 5 2 0.183 0.549 30000 189.6 180.5 97.9 92.4 22 45 3 6 0.372 1.156 22500 182.6 178.1 94.8 91.1 23 60 1 10 0.389 1.177 30000 178.4 172 92.3 89 24 45 7 6 0.412 1.256 22500 179.7 176.3 93.2 89.1 25 60 5 2 0.733 2.199 15000 184.1 178.7 92.1 87.9 26 30 1 2 0.128 0.364 30000 195.9 188.6 101.1 96.4 27 30 1 2 0.103 0.319 15000 200.8 193.6 109.6 104.3 28 60 5 2 0.781 2.373 30000 174.6 165.9 86.3 84.4 29 60 5 10 0.464 1.692 15000 195.5 186.5 94.4 90.8 30 60 1 2 0.589 1.767 15000 194.3 185.5 93.6 90.3