Influence of Sintering Temperature on Mechanical Properties of Glass-Ceramics Produced with Windshield Waste

Table 3

Flexural strength and Weibull modulus of all groups.

Group	Flexural strength (MPa)	Standard deviation (MPa)	Weibull modulus (m)	R^2
1	74.67	21.09	2.50	0.83
2	77.64	14.54	5.41	0.81
3	52.47	7.06	6.87	0.93
4	43.86	5.85	7.42	0.86
5	38.25	6.81	5.66	0.94
6	40.10	6.71	5.96	0.93
7	29.15	5.41	5.15	0.92
8	52.57	6.47	8.03	0.96