Novel Systems and Membrane Technologies for Carbon Capture
Table 1
Properties of MOFs and MOF-based membranes measured at pressures of 8.5–224.99 bar.
| Nomenclature/molecular formula | Feed composition (CH4/CO2/H2) | X (CO2 : CH4 : H2) (wt.%) or as given | High-pressure separation data | T (K) | SCO2 | Q | Ref. | BET surface area (m2/g) | Langmuir surface area (m2/g) | Adsorptive capacity (%) | P (bar) |
| UiO(bpdc) | — | 79.7 : 12.2 : 5.7 | 2646 | 2965 | 72.5 | 20 | 303 | | | [108] | ZJU-32 | — | 49 | 3831 | 49 | 40 | | 300 | | | [109] | UPG-1 | — | 72 : 69 cc/g | 410 | 514 | 11.9 | 9.8 | 298 | 24 | 24 | [110] | Cu3 (H2L2) (bipy)2 .11H2O | — | 77 cc/g | | | 6.4 | 8.5 | 298 | | | [111] | Cu3 (H2L2) (etbipy)2 .24H2O | — | 77 cc/g | | | 4.7 | 9.6 | 298 | | | [111] | NU-111 | — | 350 : 284 cc/cc feed | 4932 | | 61.8 | 30 | 298 | | 23 | [112] | HTS-MIL-101 | — | 1112 mg/g | 3482 | | 52.8 | 40 | 298 | | | [113] | DGC-MIL-101 | — | 1112 mg/g | 4198 | | 59.8 | 40 | 298 | | | [113] | UTSA-62a | 30/20/5 | 189 : 270 cc/cc of feed | 2190 | | 43.7 | 55 | 298 | | 16 | [114] | ZIF-7 | | 10.3 | 312 | 355 | 20.9 | 10 | 298 | | 33 | [115] | {Ag3[Ag5(l3-3,5-Ph2tz)6] (NO3)2}n | — | 0.025 : 0.35 mmol/g | | | 12.3 | 10 | 298 | 10.5 | 19.1 | [116] | Basolite® C 300 | 99.9% | 16 mmol/g | 1706.42 | | 41.9 | 224.99 | 318 | | 18 | [117] | Basolite® F300 | 99.9% | 16 mmol/g | 1716.46 | | 24.1 | 224.99 | 318 | | 19 | [117] | Basolite® A100 | 99.9% | 8 mmol/g | 1524.8 | | 26.9 | 224.99 | 318 | | 9 | [117] | MIL-101(Cr) | 99.99% | 1.17 mmol/g | 2549 | | 24.2 | 30 | 303 | | | [118] | HKUST-1 | 99.99% | 1.82 mmol/g | 1326 | | 26.3 | 30 | 303 | | | [118] | DMOF | — | 2.5 mol/kg | 1980 | | 38.1 | 20 | 298 | 12a | 20 | [119] | DMOF-cl2 | — | 2.15 mol/kg | 1180 | | 26.4 | 20 | 298 | 17 | 21 | [119] |
|
|
|