Review Article
Novel Systems and Membrane Technologies for Carbon Capture
Table 2
Properties of MOFs and MOF-based membranes measured at pressures of 0.91–1.01 bar.
| Nomenclature/molecular formula | Feed condition (CO2 : N2) | X (CO2 : CH4 : H2) uptake (wt.%) | Low-pressure separation data | T (K) | SCO2 | Q (kJmol−1) | Ref. | BET surface area (m2/g) | Langmuir surface area (m2/g) | Adsorptive capacity | P (bar) |
| rht-MOF-pyr | | 112 : 17 cc/g | 2100 | | 12.7 | 1 | 298 | | 28 | [120] | rht-MOF-1 | | 90 : 16.4 | 2100 | | 11 | 1 | 298 | | 29 | [120] | JLU-Liu22 | | 170 cc/g | 1487 | | 15.6 | 1 | 298 | | 30 | [121] | SIFSIX-3-Co | 15 : 85 | 62.6 cc/g | 223 | | 10 | 1 | 298 | | 47 | [122] | SIFSIX-3-Ni | — | 64.5 | 368 | | 10.3 | 1 | 298 | | 59 | [122] | {[H2N(CH3)2 ]4 [Zn9O2 (BTC)6 (H2O)3 ].3DMA}cn | — | 99 : 63 cc/g | 844 | 1132 | 10.9 | 0.91 | 298 | | 29 | [123] | {[NH2 (CH3)2, Cd(BTC)].DMA}n | — | 32 : 23 cc/g | 406 | 539 | 6.4 | 0.91 | 298 | 30 | 34.7 | [123] | Ni-DOBDC | | 2.30 mol/kg | 798 | | 18.2 | 1 | 298 | | | [124] | Py-Ni-DOBDC | | 1.64 mol/kg | 409 | | 12 | 1 | 298 | | 16 | [124] | UiO(bpdc) | — | 8 | 2646 | 2965 | 8 | 1 | 303 | | | [108] | ZJU-32 | — | 0.1 : 0.01 | 3831 | | 4.8 | 1 | 300 | | | [109] | Zn(5-mtz) (2-eim).(guest) [ZTIF-1] | | 49 : 13.16 cc/g | 1430 | 1981 | 8.2 | 1 | 295 | 81 | 22.5 | [125] | Zn(5-mtz) (2-pim).(guest) [ZTIF-2] | | 29.3 cc/g | 1287 | 1461 | 3.8 | 1 | 295 | | 20 | [125] | UTSA-49 10 : 90; 15 : 85; 20 : 80 | | 69 cc/g | 710.5 | 1046.6 | 13.6 | 1 | 298 | 95.8 | | [126] | ZJNU-40 5 : 95 | | 108 cc/g | 2209 | | 16.4 | 1.01 | 296 | | 18.4 | [127] | UPG-1 | — | 22 | 410 | 514 | 2.1 | 1 | 298 | 24 | 24 | [110] | UiO-66(Zr100) | | 2.2 mmol/g | 1390 | 1644 | 6.2 | 1 | 298 | | 26 | [128] | UiO-66(Ti32) and UiO-66(Zr/Ti) | | 2.3 and 4 mmol/g | 1418 | 1703 | 6.4 | 1 | 298 | | 28 | [128] | UiO-66(Ti44) | — | 2.3 cc/g | 1749 | 2088 | 7.2 | 1 | 298 | | 34 | [128] | JLU-Liu1 | — | 34.7 : 0.5 cc/g | 145 | 221 | 5.9 | 1 | 298 | | 47.7 | [129] | UTSA-62a 30/20/5 | | 189 : 270 cc/cc of feed | 2190 | | 8.1 | 1 | 298 | | 16 | [114] | Zn-DABCO | 60–100 mg | 1.87 mmol/g | 1870 | 1902 | 7.2 | 1 | 298 | | 22.4 | [87] | Ni-DABCO | 60–100 mg | 2.17 : 0.51 mmol/g | 2120 | 2219 | 8.1 | 1 | 298 | | 25.8 | [87] | Co-DABCO | 60–100 mg | 1.02 : 0.57 mmol/g | 2022 | 2095 | 4.1 | 1 | 298 | | 29.8 | [87] | Mg/DOBDC | 40 : 60 v/v | 180 cc/g | 1415.1 | | 25 | 1 | 298 | | 47 | [88] | {Ag3[Ag5(l3-3,5-Ph2tz)6](NO3)2}n | — | 7-8 CO2 molecules/unit adsorbent (0.39 mmol/g) | | | 1.6 | 1 | 298 | 10.5 | 19.1 | [116] | {Ag3[Ag5(l3-3,5tBu2tz)6](BF4)2}n | — | 0.37 mmol/g | | | 1.6 | 1 | 298 | 14 | 15 | [116] | Basolite® C 300 | | 2 mmol/g | 1706.42 | | 9.4 | 0.95 | 318 | | 18 | [117] | Basolite® F300 | | 0.5 mmol/g | 1716.46 | | 2,4 | 0.95 | 318 | | 19 | [117] | CPM-5 | | | 2187 | | 8.8 | 1 | 298 | 16.1 | 36.1 | [130] | ZIF-68 15 : 10 : 75 (CO2:SO2:N2) | | 1.6 mol/kg | 1220 | | 41.3 | 0.9 | 298 | 30 | 33.3 | [131] | Zn4(bpta)2-1 - | | 41.95 cm3/g | | 51 | 8.2 | 1.2 | 298 | 23 | 34.82 | [132] | Cu2L (DMA)4 UHP-grade | UHP-grade 99.99% | 160 cm3/g | 1433 | | 22.2 | 1 | 296 | 41.6 | 35 | [133] | bio-MOF-11 | 10 : 90 (CO2 : N2) | 147 cm3/g | 1148 | | 22.2 | 1 | 273 | 123 | 33.1 | [134] | bio-MOF-14 | 10 : 90 (CO2 : N2) | 44.8 cm3/g | | 17 | 8 | 1 | 273 | Extremely high | — | [134] |
|
|