Study on Susceptibility and Mechanism of Reheat Cracking in Welded Joint of Type 347 Austenitic Stainless Steel
Table 4
Welding specimen M high-temperature constant load test result.
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
Note. The reheat cracking critical fracture stress of specimen M was 24 MPa, which is much lower than 80% of the high-temperature yield strength of base material, which means the welded joint had a high reheat cracking susceptibility. |