Material | Specification | Constituent | Manufacturer |
|
Filtek Silorane posterior restorative | Visible light activated silorane based restorative composite | (i) Silorane resin | 3M ESPE Dental Product St. Paul, MN, USA |
(ii) Initiating system: camphorquinone, iodonium salt, electron donor |
(iii) Fillers: Quartz filler |
(iv) Yttrium fluoride with Average Particle Size (μm) 0.47 Filler Load by Weight (%) 76% |
(v) Stabilizers |
(vi) Pigments |
|
Silorane Adhesive Bond System | Silorane Self-etch Primer: | Phosphorylated methacrylates | 3M ESPE Dental Products St. Paul, MN, USA |
(i) Vitrebond copolymer |
(ii) BisGMA |
(iii) HEMA |
(iv) Water |
(v) Ethanol |
(vi) Silane-treated silica filler |
(vii) Initiators |
(viii) Stabilizers |
Silorane Adhesive Bond: | (i) Hydrophobic dimethacrylate | 3M ESPE Dental Products St. Paul, MN, USA |
(ii) Phosphorylated methacrylates |
(iii) TEGDMA |
(iv) Silane-treated silica filler |
(v) Initiators |
(vi) Stabilizer |
|
Filtek Z250 | Visible light activated methacrylate-based restorative composite | (i) The filler is zirconia/silica | 3M ESPE Dental Products St. Paul, MN, USA |
(ii) The inorganic filler loading is 60% by volume “without silane treatment” with particle size range of 0.01 and 3.5 microns. |
(iii) It contains Bis-GMA and TEGDMA resins. |
|
Adper Prompt L-Pop | Self-etch one-step bonding agent | Liquid 1 (red blister): | 3M ESPE Dental Products St. Paul, MN, USA |
(i) Methacrylated phosphoric esters |
(ii)Bis-GMA |
(iii) Initiators based on camphorquinone |
(iv) Stabilizers |
Liquid 2 (yellow blister): |
(i) Water |
(ii) 2-Hydroxyethyl methacrylate (HEMA) |
(iii) Polyalkenoic acid |
(iv) Stabilizers |
|