Electronic Properties of Nanoparticles Films and the Effect on Apatite-Forming Ability
Figure 1
X-ray diffraction of TiO2-synthesised nanoparticles with 8 or 22 nm size. The particles were dried at 120°C for 16 h prior to the analysis. Diffraction peaks marked with A correspond to anatase while B stands for brookite. The inset shows enlargement of the diffraction pattern for the particles dispersed on Ti (thin line). The film was washed and allowed to dry at room temperature overnight.
