Shaping Ability of Superelastic and Controlled Memory Nickel-Titanium File Systems: An In Vitro Study
Table 1
Area removed1 (mm2) for each instrument.
| Segments | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 |
| F360 | | Outer wall | 0.03 ± 0.01 | 0.04 ± 0.02 | 0.06 ± 0.02 | 0.07 ± 0.02 | 0.07 ± 0.02 | 0.05 ± 0.02 | 0.08 ± 0.03 | 0.13 ± 0.02 | 0.16 ± 0.03 | 0.16 ± 03 | Inner wall | 0.02 ± 0.01 | 0.03 ± 0.01 | 0.03 ± 0.01 | 0.04 ± 0.02 | 0.09 ± 0.03 | 0.13 ± 0.03 | 0.12 ± 0.02 | 0.10 ± 0.01 | 0.10 ± 0.01 | 0.09 ± 02 | values | 0.047 | 0.396 | 0.007 | 0.011 | 0.128 | 0.005 | 0.005 | 0.005 | 0.005 | 0.005 |
| HyFlex®CM™ | | Outer wall | 0.03 ± 0.01 | 0.03 ± 0.02 | 0.06 ± 0.02 | 0.07 ± 0.02 | 0.05 ± 0.02 | 0.04 ± 0.01 | 0.08 ± 0.01 | 0.11 ± 0.02 | 0.14 ± 0.02 | 0.15 ± 0.02 | Inner wall | 0.03 ± 0.01 | 0.04 ± 0.02 | 0.03 ± 0.01 | 0.05 ± 0.02 | 0.10 ± 0.02 | 0.13± 0.02 | 0.10 ± 0.02 | 0.08 ± 0.01 | 0.08 ± 0.02 | 0.07 ± 0.02 | values | 0.096 | 0.726 | 0.008 | 0.015 | 0.009 | 0.005 | 0.076 | 0.009 | 0.007 | 0.005 |
|
|
1Mean ± standard deviation; values are statistically significant. |