Effect of Marginal Designs on Fracture Strength of High Translucency Monolithic Zirconia Crowns
Figure 2
Zirconia crown was seated on metal die, loaded vertically from the occlusal surface in a universal testing machine with a round end hard steel punch at a crosshead speed of 0.2 mm/min to induce circumferential hoop stress (CHS) at the crown margin (a, b) until fracture (c). Fracture specimens were further examined microscopically for the analysis of fracture (d).