| | Materials | Composition | Manufacturer | Steps of application |
| | Biodentine tricalcium silicate cement | Powder: tricalcium silicate, dicalcium silicate, calcium carbonate
Zirconium oxide (radio opacifier)
Iron oxide (colouring agent)
Liquid: calcium chloride, accelerator, hydrosoluble, polymer, water reducing agent | Setodent, France | Five doses liquid and powder supplied for 30 s with a mixed amalgamator |
| | Filtek Z350XT | Organic phase: UDMA, Bis-GMA,
Bis-EMA, TEGDMA
Inorganic phase: silica (20 nm non-agglomerated/aggregated), zirconia (4–11 nm non-agglomerated/aggregated and agglomerated), clusters, zirconia/silica aggregated particles (20 nm silica particles combined with 4–11 nm zirconia)
Filler content (vol.%) 63.3% | 3M, ESPE, USA | Apply increments of 2 mm and light-cure for 20 s |
| | Tetric N-Ceram nano-hybrid | Organic phase: dimethacrylates TEGDMA
Inorganic phase: barium aluminum silicate glass (0.4–0.7 μm), ytterbium trifluoride (200 nm), mixed oxides (160 nm) and copolymers 80–81 barium glass filler, ytterbium trifluoride, mixed oxide (0.04–3.0 nm) Bis-GMAb, Bsis-EMA | IvoclarVivadent, Liechtenstein | Apply increments of 2 mm and light-cure for 20 s |
| | Tetric N-bond self-etch | Bis-acrylamide derivative, bis-methacrylamide dihydrogenphosphate, amino acid acrylamide, hydroxyalkyl metharylamide, nano-filler, water, stabilizers | IvoclarVivadent, Liechtenstein | Apply bonding agent and rub for 20 seconds air dry for 5 sec
Light cure for 10 sec |
| | Xeno V+ | Bifunctional acrylate, acidic acrylate, functionalized phosphoric acid ester, water, tertiary butanol, initiator, stabilizer. | Dentsply, Germany | Apply it sufficiently pooling then gently agitate the adhesive for 20 sec. Evaporate solvent thoroughly and cure for 10 seconds |
| | Bond force | Phosphoric acid Monomer, Bisphenol a di (2-hydroxypropoxy) dimethacrylate (Bis-GMA), triethylene glycol dimethacrylate, HEMA, camphorquinone, alcohol, water. | Tokuyama dental Tokyo, Japan | Apply bonding agent and rub for 20 seconds
Weak air dry for 5 sec.
Strong air dry for 5+ sec. And light cure for 10 sec |
|
|