Physicomechanical Characterization of a Novel Resin-Modified Glass Ionomer Luting Cement Functionalized with a Phosphate Functional Monomer

Table 3

Mean values and standard deviations of experimental cement’s setting time (min) and film thickness (µm).

Groups (n = 5)	Film thickness (µm)	Setting time (min)
2-MEP 0	14.5 ± (0.2)	5.65 ± (0.3)
2-MEP 10	14.7 ± (0.1)	5.50 ± (0.2)
2-MEP 20	± (0.1)	5.33 ± (0.1)
2-MEP 30	± (0.2)	± (0.08)
2-MEP40	± (0.2)	± (0.30)

Note. Represents the mean values, which are statistically significant compared to the control group at .