Scanning Electrochemical Microscopy as a Tool for the Characterization of Dental Erosion
Figure 4
SECM 2D images obtained with a platinum microelectrode ( μm) in a 0.2 mmol L−1 H2SO4 + 0.1 mol L−1 KCl solution (pH = 3.4) for an insulating substrate (a) and a tooth sample at different times: 0 minutes (b), 60 minutes (c), and 70 minutes (d). Image (d) was recorded after solution stirring. Scan rate = 20 μm s−1.