Electrodeposition of Oriented Cerium Oxide Films
Figure 10
SEM morphologies for CeO2 deposited with galvanostatic mode at 80°C, j = −0.06 mA/cm2; (a) unsintered: x7500; (b) sintered 500°C: x7500; (c) sintered at 900°C: x7500; (d) sintered at 1100°C: x7500.