Influence of Bath Composition at Acidic pH on Electrodeposition of Nickel-Layered Silicate Nanocomposites for Corrosion Protection
Figure 5
Tafel plot of Ni-MMT (0.5%) films measured in 3.5% NaCl solution at 25°C. Coatings were electrodeposited from a plating solution at various pHs (1.6, 2.5, and 3.0) onto stainless steel substrates.