| Material | Environment | Method | Rate, m/year |
| Steel | Type I water, 0°C | Corrosion current by Tafel method | 58 | Steel | Type I water, 10°C | Corrosion current by Tafel method | 93 | Steel | Type I water, 20°C | Corrosion current by Tafel method | 180 | Steel | Type I water, 0°C, diluted 1 : 6 | Corrosion current by Tafel method | 46 | Steel | Type I water, 10°C, diluted 1 : 6 | Corrosion current by Tafel method | 60 | Steel | 3.5% NaCl, 20°C, 14-day test | Corrosion current by LPR | 280 | Steel | 3.5% NaCl, 20°C, 28-day test | Corrosion current by LPR | 310 | Steel | 3.5% NaCl, 20°C, 14-day test | Weight loss | 70 | Steel | 3.5% NaCl, 20°C, 28-day test | Weight loss | 52 | AISI 316L | Type I water, 0°C | Corrosion current by Tafel method | <2 | AISI 316L | Type I water, 10°C | Corrosion current by Tafel method | <2 | AISI 316L | Type I water, 0°C, diluted 1 : 6 | Corrosion current by Tafel method | <2 | AISI 316L | Type I water, 10°C, diluted 1 : 6 | Corrosion current by Tafel method | <2 | AISI 316L | 3.5% NaCl, 20°C | Corrosion current by LPR | <1 |
|
|