Microstructure, Strength, and Fracture Topography Relations in AISI 316L Stainless Steel, as Seen through a Fractal Approach and the Hall-Petch Law

<div>Optical micrographs of microstructures of AISI 316L austenitic stainless steel heat-treated at (a) 904°C, (b) 1010°C, (c) 1095°C, and (d) 1194°C.</div>