Fluorescence Properties and Synthesis of Green-Emitting Tb<sup>3+</sup>-Activated Amorphous Calcium Silicate Phosphor by Ultraviolet Irradiation of 378 nm

<table>Effect of initial Tb/Ca atomic ratio on the emission intensity of the phosphor heated at 700°C.</table>

International Journal of Optics

fig3

Figure 3

Figure 3: Fluorescence Properties and Synthesis of Green-Emitting Tb<sup>3+</sup>-Activated Amorphous Calcium Silicate Phosphor by Ultraviolet Irradiation of 378 nm 

Figure 3 | Fluorescence Properties and Synthesis of Green-Emitting Tb3+-Activated Amorphous Calcium Silicate Phosphor by Ultraviolet Irradiation of 378 nm 