Enhancement of Photon Absorption on Ba_𝑥Sr_1−𝑥TiO₃ Thin-Film Semiconductor Using Photonic Crystal

Table 2

Electrical conductivity value (σ) of BST thin films after exposed by light with intensity more than 2000 lux (bright condition).

Mole fraction (𝑥)	𝜎 (×10^−1 S/cm)				Reduction percentage 𝜎 (%)
	Dark		Bright
	A	B	A	B	A	B
0.25	0.57125	0.22525	0.24813	0.20508	130,22206	9,83519
0.35	5.10250	0.51025	3.25333	0.43117	56,83930	18,34079
0.45	4.96366	1.05475	1.21908	1.03142	307,16442	2,26193
0.55	3.50833	1.86517	2.10444	1.08008	66,71086	72,68813

Conducted relatively to mole fraction 𝑥=0.25; A: without photonic crystals layer; B: with photonic crystals layer.