Effect of Gold Dispersion on the Photocatalytic Activity of Mesoporous Titania for the Vapor-Phase Oxidation of Acetone
Table 1
Physical properties of TiO2 and Au/TiO2 samples.
Sample
Calcination Temp. (K)
Au content (wt%)
Surface area (m2g-1)
Average crystallite size (nm)
Average gold particle size (nm)
Average pore diameter (nm)
Initial
Final
T1
623
–-
109
9.6
–-
4.2
H1
375
1.0
0.6
–-
–-
–-
–-
H2
523
1.0
0.6
214.4
5.2
1.0
3.5, 2.4
H3
623
1.0
0.6
157.0
4.4
1.0
3.3, 1.6
H4
773
1.0
0.6
–-
10.8
–-
–-
H5
623
1.5
0.8
66.1
11.3
5.7
3.8
H6
623
2.0
1.3
65.0
8.7
–-
–-
I1
623
1.0
1.1
74.7
7.1
7.5
4.7
I2
623
1.5
1.7
35.7
7.0
–-
4.5
I3
623
2.0
2.1
39.4
7.0
9.0
4.5
TiO2 sample prepared by hydrothermal route. Au/TiO2 with gold incorporated during hydrothermal process. Au/TiO2 with gold dispersed over sample T1 by impregnation. From XRD data using Scherrer’s equation. From TEM results. From N2 adsorption data.