Characterizations of Chitosan-Based Polymer Electrolyte Photovoltaic Cells
Table 2
Characteristics of PEC cells using polymer-salt systems.
| Sample | Dye | Intensity (mW cm−2) | Redox couple | (S cm−1) | (mA cm−2) | OCV (V) | ff | (%) | Ref. |
| 91 wt.% Poly(butyl acrylate) + 9 wt.% NaI | Ru(dcbpy)2(NCS)2 | 100 | | | 2.20 | 0.61 | 0.37 | 0.51 | [37] | 87.5 wt.% PEO + 12.5 wt.% NaI | Ru(dcbpy)2(NCS)2 | 100 | | | 1.51 | 0.83 | 0.61 | 0.76 | [38] | 92 wt.% PEO + 8 wt.% KI | Ru(dcbpy)2(NCS)2 | 100 | | | 5.04 | 0.62 | 0.63 | 1.96 | [1] | 89 wt.% P(EPI-EO) + 11 wt.% NaI | Ru(dcbpy)2(NCS)2 | 100 | | | 0.55 | 0.75 | — | 0.19 | [9] | 71 wt.% P(EPI-EO) + 29 wt.% NaI | Ru(dcbpy)2(NCS)2 | 120 | | | 0.46 | 0.71 | 0.67 | 0.22 | [39] | 55 wt.% Chitosan + 45 wt.% | None | 56.4 | | | 0.005 | 0.15 | 0.22 | — | [35] |
|
|