Characterizations of Chitosan-Based Polymer Electrolyte Photovoltaic Cells
Table 3
Characteristics of PEC cells using plasticized polymer-salt systems.
| Polymer electrolyte Sample | Dye | Intensity (mW cm−2) | Redox couple | (S cm−1) | (mA cm−2) | OCV (V) | ff | (%) | Ref. |
| 27.2 wt.% PEO + 2.8 wt.% wt.% EC | Ru(dcbpy)2(NCS)2 | 100 | | | 0.051 | 0.44 | 0.48 | 0.01 | [40] | | Ru(dcbpy)2(NCS)2 | 27 | | | 2.10 | 0.60 | 0.62 | 2.90 | [41] | 13.5 wt.% PAN + 7.3 wt.% wt.% EC + 46.9 wt.% PC | Ru(dcbpy)2(NCS)2 | 60 | | | 3.73 | 0.69 | — | 2.99 | [42] | 43.5 wt.% P(EPI-EO) + 13 wt.% NaI + 43.5 wt.% P(EGME) | Ru(dcbpy)2(NCS)2 | 100 | | | 1.88 | 0.7 | — | 0.52 | [9] | 33 wt.% chitosan + 27 wt.% wt.% EC | None | 56.4 | | | 0.007 | 0.22 | 0.18 | — | [35] |
|
|