Development of Well-Aligned TiO2 Nanotube Arrays to Improve Electron Transport in Dye-Sensitized Solar Cells
Table 1
Photovoltaic and kinetic parameters of cell type-A, and cell type-B based DSSCs.
| DSSCs | Photoelectrode | (mA/cm2) | (mV) | FF (%) | η (%) | (S−1) |
| Cell type-A | TNP (17 μm) | 9.32 | 815 | 71.75 | 5.45 | 13.7 | TNT (8 μm) + TNP (6 μm) | 11.50 | 848 | 66.57 | 6.50 | 11.2 | TNT (11 μm) + TNP (6 μm) | 11.68 | 837 | 68.79 | 6.72 | 11.2 | TNT (15 μm) + TNP (6 μm) | 12.56 | 853 | 71.76 | 7.70 | 11.2 | Cell type-B | TNP (7.5 μm) | 7.16 | 722 | 70.23 | 3.63 | 24.7 | TNP (13 μm) | 8.78 | 684 | 70.45 | 4.23 | 32.4 | TNP + 1 wt% TNT (8 μm) | 8.88 | 714 | 69.92 | 4.44 | 18.6 |
|
|