High Improvement in Conversion Efficiency of <i>μ</i>c-SiGe Thin-Film Solar Cells with Field-Enhancement Layers

<table><i>J</i>-<i>V</i> measurements of <i>μ</i>c-Si<sub>0.9</sub>Ge<sub>0.1</sub>:H solar cells with <i>μ</i>c-Si:H FEL varied from 0 to 300 nm.</table>