Fabrication of Large-Grain Thick Polycrystalline Silicon Thin Films via Aluminum-Induced Crystallization for Application in Solar Cells
Figure 4
SEM images and EDS results of induced poly-Si thin films annealed for various durations: (a) 15 min, top view; (b) 15 min, cross-sectional view; (c) 15 min, EDS results; (d) 120 min, top view; (e) 120 min, cross-sectional view; and (f) 120 min, EDS results.