Glass Frit Dissolution Influenced by Material Composition and the Water Content in Iodide/Triiodide Electrolyte of Dye-Sensitized Solar Cells
Figure 5
Absorbance at 430 nm as a function of time for the test cells filled with solvent, nonaqueous redox electrolyte, and redox electrolyte with 1, 5, and 10 wt% H2O. (a) Test cell with GF2. Absorbance decreases over time for cells with 1, 5, and 10 wt% H2O in electrolyte. (b) Test cell with GF3. Absorbance decreases over time for cells with 5 and 10 wt% H2O in electrolyte.