Volume 2014, Article ID 197824, 7 pages
http://dx.doi.org/10.1155/2014/197824
Research Article

Synthesis, Characterization, and Photocatalytic Activity of Zn-Doped SnO2/Zn2SnO4 Coupled Nanocomposites

1Department of Materials Science and Engineering, Luoyang Institute of Science and Technology, Luoyang 471023, China
2State Key Lab of Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China
3School of Materials Science and Engineering, Chongqing University of Technology, Chongqing 400050, China

Received 31 May 2013; Revised 8 November 2013; Accepted 11 November 2013; Published 28 January 2014

Academic Editor: Peter Robertson

Copyright © 2014 Tiekun Jia et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

Zn-doped SnO2/Zn2SnO4 nanocomposites were prepared via a two-step hydrothermal synthesis method. The as-prepared samples were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), UV-vis diffuse reflection spectroscopy, and adsorption-desorption isotherms. The results of FESEM and TEM showed that the as-prepared Zn-doped SnO2/Zn2SnO4 nanocomposites are composed of numerous nanoparticles with the size ranging from 20 nm to 50 nm. The specific surface area of the as-prepared Zn-doped SnO2/Zn2SnO4 nanocomposites is estimated to be 71.53 m2/g by the Brunauer-Emmett-Teller (BET) method. The photocatalytic activity was evaluated by the degradation of methylene blue (MB), and the resulting showed that Zn-doped SnO2/Zn2SnO4 nanocomposites exhibited excellent photocatalytic activity due to their higher specific surface area and surface charge carrier transfer.

1. Introduction

Since the discovery of photoelectrochemical water splitting using TiO2 electrodes [1], the investigation of the development of oxide semiconductor photocatalysts used for the degradation of environmental organic pollutants has attracted considerable attention for the past two decades [28]. Recently, Zn2SnO4 is considered to be a promising photocatalyst due to its high electron mobility, high electrical conductivity, and favorable stability in acidic and basic solutions [913]. It is reported that Zn2SnO4 nanostructures were used to decompose organic pollutants under UV light irradiation in previous studies [11, 12]. Ai et al. proposed a hydrothermal route to synthesize Zn2SnO4 microcubes and the photocatalytic activity of Zn2SnO4 microcubes was evaluated by the degradation of NO and HCHO under UV-vis light irradiation [11]. Tian et al. prepared Zn2SnO4 and Zn2SnO3 nanostructures by the combined strategy of laser ablation and hydrothermal treatment, and the results showed that Zn2SnO3 was active and effective for the degradation of methyl orange [12]. However, the fast recombination rate of the photogenerated electron/hole pairs of Zn2SnO4 prohibits the desirable photocatalytic activity. It is generally accepted that the technique of coupled oxides with different band gap widths is an effective approach to enhance the photocatalytic activity by increasing the separation of recombination rate of the photogenerated electron/hole pairs and extending the energy range of the photoexcitation [1417]. Zn2SnO4 and SnO2 have been investigated for the degradation of organic pollutants [11, 12, 1821], and they have availably matched band gap widths for coupled composites [18, 19]. Additionally, the photocatalytic activity of SnO2 can be enhanced by the zinc dopant ions incorporation into the lattice [20, 21]. Additionally, there are few reports on the synthesis and photocatalytic activity of Zn-doped SnO2/Zn2SnO4.

Herein, we reported a two-step hydrothermal synthesis route for the preparation of Zn-doped SnO2/Zn2SnO4 nanocomposites. The photocatalytic activity of the samples was evaluated by the degradation of MB, and the degradation process of MB was investigated in detail. To the best of our knowledge, this is the first time to report the preparation and photocatalytic activity of Zn-doped SnO2/Zn2SnO4 nanocomposites.

2. Experimental Details

2.1. Preparation of Zn-Doped SnO2

The preparation of Zn-doped SnO2 was also described in our previous studies [21]. All the reagents were analytically pure, purchased from Shanghai chemical industrial company, and used as received. In a typical procedure, 24 mmol NaOH was dissolved in 80 mL of mixed solvents containing 60% water and 40% ethanol. 3.43 mmol SnCl4·5H2O was added to the mixed solution under rigorous stirring. After constant stirring for 30 min, 0.57 mmol Zn (NO3)2·6H2O was introduced into the mixed solution. After another 30 min of stirring, the obtained precursor was transferred into a 100 mL Teflon-lined stainless steel autoclave, and was put into an electric oven. The autoclave was maintained at 180°C for 20 h and cooled naturally to room temperature. The products were centrifuged and washed with distilled water and ethanol for several times, followed by drying in a vacuum oven at 60°C for 12 h.

2.2. Preparation of Zn-Doped SnO2/Zn2SnO4

In a typical procedure, 2 mmol tin (IV) chloride pentahydrate (SnCl4·5H2O) and 4 mmol zinc acetate dihydrate (Zn (AC)2·2H2O) were dissolved in 20 mL mixed solvents of water and ethanol (volume ratio of 4 : 1) to form two transparent solutions, respectively. The above solutions were mixed together under magnetic stirring. A certain amount of the as-prepared Zn-doped SnO2 was added into the mixed solution (Zn-doped SnO2/Zn2SnO4 = 15 wt%). Then, 16 mmol sodium hydroxide (NaOH) was dissolved in 40 mL mixed solvents of water and ethanol (volume ratio of 4 : 1) to make a clear solution. In the next step, the NaOH solution was slowly dropped into the above mixed solution under magnetic stirring, and then the above solution was mixed by a magnetic stirrer for 1 hour. The obtained white suspension was transferred to Teflon-lined stainless steel autoclave with 100 mL capacity and heated at the temperature of 200°C for 15 h. After the autoclave had cooled naturally to room temperature, the final precipitates were centrifuged and washed with distilled water and ethanol, respectively, followed by drying under vacuum at 60°C for 12 h. Additionally, pure Zn2SnO4 was also obtained via a similar hydrothermal synthesis route without adding Zn-doped SnO2.

2.3. Characterization

XRD pattern was carried out on a Rigaku ultima III diffraction meter equipped with Cu Kα radiation ( mn). FESEM images were taken using a Hitachi S-4800 field emission scanning electron microscope. TEM images were recorded on a JEM 2100 transmission electron microscope. The nitrogen adsorption and desorption isotherms at 77 K were measured using a Quantachrome NOVA 2000e sorption analyzer after samples were vacuum-dried at 473 K overnight. UV-vis diffuse reflectance spectra were recorded on a UV-vis spectrophotometer (UV2500, Shimadzu). The photoluminescence (PL) spectra were measured using a Hitachi F-4600 fluorescence spectrophotometer.

2.4. Photocatalytic Experiments

The photocatalytic activity was evaluated by the decolorization of MB aqueous solution. As reported in our previous work [21, 22], 20 mL MB aqueous solution with a concentration of 1.0 × 10−5 M was added into the dish with 0.1 g prepared catalyst. A UV lamp (15 W, 365 nm) was used as light source to trigger the photocatalytic reaction. After irradiating for a certain time, the reacted solution was filtrated to measure the concentration variation of MB by recording the variation of the intensity of absorption peak centered at 664 nm using UV-visible spectrophotometer (UV-2550, Shimadzu, Japan). Consulting the literatures [2325], the photodegradation efficiency of MB was evaluated by , where is concentration of the MB solution at reaction time and is the adsorption/desorption equilibrium concentration of MB (at reaction time 0).

3. Results and Discussion

3.1. Phase and Morphology

XRD patterns of Zn-doped SnO2, Zn2SnO4, and Zn-doped SnO2/Zn2SnO4 nanocomposites are shown in Figure 1, respectively. From Figure 1, it can be found that the diffraction peaks in the pattern of Zn-doped SnO2 are assigned to the tetragonal rutile structure of SnO2 with lattice parameters comparable to the standard values (JCPDS, number 77-0451). Meanwhile, the characteristic peaks of Zn2SnO4 including (110), (220), (311), (222), (400), (422), (511), and (440) are in good accordance with the standard card of cubic Zn2SnO4 (JCPDS number 74-2184). For Zn-doped SnO2/Zn2SnO4 nanocomposites, additional characteristic peaks with 2 values of 26.36° and 33.86° appeared, which could be indexed to the (110) and (101) crystal planes of SnO2. No other impurities peaks are found in Zn-doped SnO2/Zn2SnO4 nanocomposites, suggesting that the nanocomposites have a two-phase composition: Zn2SnO4 and Zn-doped SnO2.

197824.fig.001
Figure 1: XRD patterns of as-prepared Zn-doped SnO2, Zn2SnO4, and Zn-doped SnO2/Zn2SnO4 nanocomposites.

Figure 2 shows the FESEM and TEM images of Zn-doped SnO2/Zn2SnO4 nanocomposites prepared via a two-step hydrothermal synthesis method. As seen in the typical FESEM image at low magnification (Figure 2(a)), the as-prepared Zn-doped SnO2/Zn2SnO4 nanocomposites are composed of monodispersed and uniform nanoparticles. Figure 2(b) is the FESEM image at high magnification, which shows that the surfaces of the as-prepared Zn-doped SnO2/Zn2SnO4 nanocomposites are rough. Furthermore, it is clearly observed that the size of the nanoparticles ranges from 25 nm to 50 nm from Figure 2(c), suggesting that the Zn-doped SnO2/Zn2SnO4 nanocomposites might have larger surface area.

fig2
Figure 2: FESEM and TEM images of the Zn-doped SnO2/Zn2SnO4 nanocomposites: (a) the panoramic FESEM image; (b) the high magnification FESEM image; and (c) TEM image.
3.2. BET Surface Area and Pore Volume

The specific surface area and pore structure of the as-prepared Zn-doped SnO2/Zn2SnO4 nanocomposites were investigated by nitrogen adsorption-desorption isotherm. Figure 3 shows the nitrogen adsorption-desorption isotherm with its pore size distribution in the inset. It is clear that the as-prepared Zn-doped SnO2/Zn2SnO4 nanocomposites exhibit the type IV isotherm with type H3 hysteresis loop for the relative pressure in the range of 0.6–1 according to Brunauer-Deming-Deming-Teller (BDDT) classification [15, 26], revealing the characteristic of mesoporous materials and the presence of mesopores (2–50 nm) [27]. The specific surface area estimated by Brunauer-Emmett-Teller method is 71.53 m2/g. Furthermore, the observed hysteresis loop approaches indicating the presence of macropores (>50 nm) [27], which is in good agreement with the result of the corresponding pore size distribution of the sample in the inset of Figure 3. Additionally, the above macropores might result from the gaps between Zn-doped SnO2/Zn2SnO4 nanoparticles.

197824.fig.003
Figure 3: Nitrogen adsorption-desorption isotherm with its corresponding pore size distribution in the inset of the Zn-doped SnO2/Zn2SnO4 nanocomposites.
3.3. UV-vis and PL Spectra

Figure 4 shows UV-vis absorbance spectra of pure Zn2SnO4 and Zn-doped SnO2/Zn2SnO4 nanocomposites. The band gaps of pure Zn2SnO4 and Zn-doped SnO2/Zn2SnO4 nanocomposites are estimated at 3.58 eV and 3.60 eV, respectively. The band gap of Zn-doped SnO2/Zn2SnO4 nanocomposites is slightly higher than that of pure Zn2SnO4, which may be attributed to the synergistic effect of Zn-doped SnO2 coupled with Zn2SnO4 homogeneous nanocomposites [28, 29].

197824.fig.004
Figure 4: UV-vis absorbance spectra of pure Zn2SnO4 and Zn-doped SnO2/Zn2SnO4 nanocomposites.

To investigate the separation capacity of photogenerated carrier in nanocomposites, PL spectra of pure Zn2SnO4 and Zn-doped SnO2/Zn2SnO4 nanocomposites were measured and the results are given in Figure 5. Two asymmetric peaks centered at 410 nm and 472 nm are observed from Figure 5, whereas the band to band emission peak (~360 nm) is not found in the curve. Consulting the literature [30, 31], the two peaks can be attributed to oxygen vacancies or surface states. It is also clear from Figure 5 that Zn-doped SnO2/Zn2SnO4 nanocomposites exhibited lower emission intensity than that of pure Zn2SnO4 in the range of 400 nm and 500 nm. The above results reveal that the recombination of the photogenerated carriers in the composites decreased and a synergistic effect occurred between Zn-doped SnO2 and Zn2SnO4 that favored the electron transfer [28, 29].

197824.fig.005
Figure 5: PL spectra of pure Zn2SnO4 and Zn-doped SnO2/Zn2SnO4 nanocomposites.
3.4. Photocatalytic Activity

Figure 6 presents the variations of adsorption spectra of aqueous MB in the presence of pure Zn2SnO4, Zn-doped SnO2, and Zn-doped SnO2/Zn2SnO4 nanocomposites under ultraviolet irradiation with the wavelength 365 nm. As seen in Figure 6(a), the intensity of the characteristic adsorption peak of MB at around 663 nm decreased with the irradiation time in the degradation process. Meanwhile, the color of the suspension faded away gradually with the irradiation time prolonging in the experiment. The characteristic adsorption peak disappeared, suggesting that the MB aqueous solution was degraded completely when the irradiation time reached 120 min. Figure 6(b) shows the photocatalytic performance of different photocatalysts with otherwise identical conditions under ultraviolet irradiation with the wavelength 365 nm. Blank test (MB without any catalyst) exhibited little photolysis. Meanwhile, the decrease of MB with Zn2SnO4 in the dark was similar to that of the blank test, which demonstrated that the adsorption of MB on the as-prepared photocatalysts was negligible after the adsorption-desorption equilibrium was reached. Additionally, the photocatalytic activities of pure Zn2SnO4 and Zn-doped SnO2 were also performed to demonstrate the photocatalytic activity of Zn-doped SnO2/Zn2SnO4. It is clear from Figure 6(b) that the Zn-doped SnO2/Zn2SnO4 exhibited higher photocatalytic activities than that of pure Zn2SnO4 and pure Zn-doped SnO2. Concerning the catalyst of pure Zn2SnO4, the complete degradation of MB was achieved when the irradiation time was 180 min.

fig6
Figure 6: (a) The variations of adsorption spectra of aqueous MB in the presence of Zn-doped SnO2/Zn2SnO4 nanocomposites at different periods of time under ultraviolet irradiation; (b) the comparisons of photocatalytic degradation activity of different photocatalysts, including pure Zn2SnO4, pure Zn-doped SnO2, and 15% Zn-doped SnO2/Zn2SnO4 nanocomposites.

It is well known that the augment of specific surface area and band gap is helpful for the improvement of photocatalytic activity [3234]. In this experiment, pure Zn2SnO4 and Zn-doped SnO2/Zn2SnO4 nanocomposites obtained via a similar hydrothermal synthesis route have similar specific surface area. Meanwhile, combined with the analysis of the UV-vis spectra, the value of the band gap of pure Zn2SnO4 is very close to that of Zn-doped SnO2/Zn2SnO4 nanocomposites. Consequently, it can be inferred that surface area and band gap would have little effect on the photocatalytic performance of the above two catalysts. Based on the analysis, the enhanced photocatalytic activity can be explained as follows. The band gaps of Zn2SnO4 and Zn-doped SnO2 have matched band potentials of coupling semiconductor. On the basis of the energy diagram reported in previous literature [10, 1719], a proposed energy band structure diagram of the nanocomposites was elucidated schematically in Figure 7. Under UV light irradiation, Zn-doped SnO2 and Zn2SnO4 would be excited simultaneously and generated electron-hole pairs. As observed in Figure 7, the photogenerated electrons transfer occurred from CB of Zn-doped SnO2 to the CB of Zn2SnO4 through the interface, whereas the photo-generated holes transfer occurred from VB of Zn2SnO4 to the VB of Zn-doped SnO2 conversely, which led to the efficient separation of the photogenerated electrons and holes. Thus, the recombination rate of photoinduced charge carriers was suppressed significantly, which is also in good agreement with the result of PL spectra. Furthermore, the efficient charge separation could prolong the life time of the charge carriers and enhance the efficiency of the interfacial charge transfer to adsorbed substrates and then account for the higher photocatalytic activity of Zn-doped SnO2/Zn2SnO4 nanocomposites. Additionally, it is noteworthy to be mentioned that the introduction of zinc ions is beneficial for the enhanced photocatalytic activity of the nanocomposites.

197824.fig.007
Figure 7: Schematic diagram for the illustration of the energy band structure and photogenerated electron hole pair separation in the Zn-doped SnO2/Zn2SnO4 nanocomposites [10, 1719].

4. Conclusions

In summary, Zn-doped SnO2/Zn2SnO4 nanocomposites were successfully prepared via a two-step hydrothermal synthesis route. The as-prepared nanocomposites are composed of numerous nanoparticles with the size ranging from 20 nm to 50 nm with higher specific surface area. The investigation of the photocatalytic activity indicated that the as-prepared Zn-doped SnO2/Zn2SnO4 nanocomposites exhibit enhanced photocatalytic activities in the degradation of MB under UV light irradiation compared with that of pure Zn2SnO4, which is ascribed to the effective separation of photoinduced electron hole pairs.

Conflict of Interests

The authors declared that they do not have a direct financial relation with the commercial identities mentioned in this paper that might lead to any conflict of interests for any of the authors.

Acknowledgments

The authors express grateful thanks to the National Natural Science Foundation of China (Grants U1304520, 51102289, and 11204122) and the State Key Lab of Materials Synthesis and Processing of Wuhan University of Technology for the fund support.

References

  1. A. Fujishima and K. Honda, “Electrochemical photolysis of water at a semiconductor electrode,” Nature, vol. 238, no. 5358, pp. 37–38, 1972. View at Publisher · View at Google Scholar · View at Scopus
  2. Z. Zou, J. Ye, K. Sayama, and H. Arakawa, “Direct splitting of water under visible light irradiation with an oxide semiconductor photocatalyst,” Nature, vol. 414, no. 6864, pp. 625–627, 2001. View at Publisher · View at Google Scholar · View at Scopus
  3. R. Asahi, T. Morikawa, T. Ohwaki, K. Aoki, and Y. Taga, “Visible-light photocatalysis in nitrogen-doped titanium oxides,” Science, vol. 293, no. 5528, pp. 269–271, 2001. View at Publisher · View at Google Scholar · View at Scopus
  4. J. Yu, Q. Xiang, and M. Zhou, “Preparation, characterization and visible-light-driven photocatalytic activity of Fe-doped titania nanorods and first-principles study for electronic structures,” Applied Catalysis B, vol. 90, no. 3-4, pp. 595–602, 2009. View at Publisher · View at Google Scholar · View at Scopus
  5. X. Zhou, J. Shao, and B. Wan, “A one-step electrochemical method for the production of TiO2−xNx nanotubes,” Journal of Electrochemical Society, vol. 160, no. 6, pp. H335–H337, 2013. View at Publisher · View at Google Scholar
  6. J. Qian, G. Cui, M. Jing, Y. Wang, M. Zhang, and J. Yang, “Hydrothermal synthesis of nitrogen-doped titanium dioxide and evaluation of its visible light photocatalytic activity,” International Journal of Photoenergy, vol. 2012, Article ID 198497, 6 pages, 2012. View at Publisher · View at Google Scholar · View at Scopus
  7. J. Wei, B. Huang, P. Wang et al., “Photocatalytic properties of nitrogen-doped Bi12TiO20 synthesized by urea addition sol-gel method,” International Journal of Photoenergy, vol. 2012, Article ID 135132, 8 pages, 2012. View at Publisher · View at Google Scholar · View at Scopus
  8. J. Zhang, Z. H. Hang, Y. Xu, and F. Kang, “Hydrothermal synthesis of iodine-doped Bi2WO6 nanoplates with enhanced visible and ultraviolet-induced photocatalytic activities,” International Journal of Photoenergy, vol. 2012, Article ID 915386, 12 pages, 2012. View at Publisher · View at Google Scholar
  9. M. A. Alpuche-Aviles and Y. Wu, “Photoelectrochemical study of the band structure of Zn2SnO4 prepared by the hydrothermal method,” Journal of the American Chemical Society, vol. 131, no. 9, pp. 3216–3224, 2009. View at Publisher · View at Google Scholar · View at Scopus
  10. X. Y. Liu, H. W. Zheng, Z. L. Zhang, X. S. Liu, R. Q. Wan, and W. F. Zhang, “Effect of energy level matching on the enhancement of photovoltaic response about oxide/Zn2SnO4 composites,” Journal of Materials Chemistry, vol. 21, pp. 4108–4116, 2011. View at Publisher · View at Google Scholar · View at Scopus
  11. Z. Ai, S. Lee, Y. Huang, W. Ho, and L. Zhang, “Photocatalytic removal of NO and HCHO over nanocrystalline Zn2SnO4 microcubes for indoor air purification,” Journal of Hazardous Materials, vol. 179, no. 1–3, pp. 141–150, 2010. View at Publisher · View at Google Scholar · View at Scopus
  12. Z. Tian, C. Liang, J. Liu, H. Zhang, and L. Zhang, “Zinc stannate nanocubes and nanourchins with high photocatalytic activity for methyl orange and 2,5-DCP degradation,” Journal of Materials Chemistry, vol. 22, no. 33, pp. 17210–17214, 2012. View at Publisher · View at Google Scholar
  13. H. Zhu, D. Yang, G. Yu, H. Zhang, D. Jin, and K. Yao, “Hydrothermal synthesis of Zn2SnO4 nanorods in the diameter regime of sub-5 nm and their properties,” Journal of Physical Chemistry B, vol. 110, no. 15, pp. 7631–7634, 2006. View at Publisher · View at Google Scholar · View at Scopus
  14. H. Wang, S. Baek, J. Lee, and S. Lim, “High photocatalytic activity of silver-loaded ZnO-SnO2 coupled catalysts,” Chemical Engineering Journal, vol. 146, no. 3, pp. 355–361, 2009. View at Publisher · View at Google Scholar · View at Scopus
  15. H. Yu, R. Liu, X. Wang, P. Wang, and J. Yu, “Enhanced visible-light photocatalytic activity of Bi2WO6 nanoparticles by Ag2O cocatalyst,” Applied Catalysis B, vol. 111-112, no. 28, pp. 326–333, 2012. View at Publisher · View at Google Scholar · View at Scopus
  16. J. Yu and J. Ran, “Facile preparation and enhanced photocatalytic H2-production activity of Cu(OH)2 cluster modified TiO2,” Energy and Environmental Science, vol. 4, no. 4, pp. 1364–1371, 2011. View at Publisher · View at Google Scholar · View at Scopus
  17. C. Wang, C. Shao, Y. Liu, and X. Li, “Water-dichloromethane interface controlled synthesis of hierarchical rutile TiO2 superstructures and their photocatalytic properties,” Inorganic Chemistry, vol. 48, no. 3, pp. 1105–1113, 2009. View at Publisher · View at Google Scholar · View at Scopus
  18. T. J. Coutts, D. L. Young, X. Li, W. P. Mulligan, and X. Wu, “Search for improved transparent conducting oxides: a fundamental investigation of CdO, Cd2SnO4, and Zn2SnO4,” Journal of Vacuum Science and Technology A, vol. 18, no. 6, pp. 2646–2660, 2000. View at Publisher · View at Google Scholar · View at Scopus
  19. R. Könenkamp, R. C. Word, and M. Godinez, “Electroluminescence in nanoporous TiO2 solid-state heterojunctions,” Nanotechnology, vol. 17, no. 8, pp. 1858–1861, 2006. View at Publisher · View at Google Scholar · View at Scopus
  20. Z. Wen, G. Wang, W. Lu, Q. Wang, Q. Zhang, and J. Li, “Enhanced photocatalytic properties of mesoporous SnO2 induced by low concentration ZnO doping,” Crystal Growth and Design, vol. 7, no. 9, pp. 1722–1725, 2007. View at Publisher · View at Google Scholar · View at Scopus
  21. T. Jia, W. Wang, F. Long, Z. Fu, H. Wang, and Q. Zhang, “Synthesis, characterization, and photocatalytic activity of Zn-doped SnO2 hierarchical architectures assembled by nanocones,” Journal of Physical Chemistry C, vol. 113, no. 21, pp. 9071–9077, 2009. View at Publisher · View at Google Scholar · View at Scopus
  22. T. Jia, W. Wang, F. Long, Z. Fu, H. Wang, and Q. Zhang, “Fabrication, characterization and photocatalytic activity of La-doped ZnO nanowires,” Journal of Alloys and Compounds, vol. 484, no. 1-2, pp. 410–415, 2009. View at Publisher · View at Google Scholar · View at Scopus
  23. H. Xu, Y. Xu, H. Li et al., “Synthesis, characterization and photocatalytic property of AgBr/BiPO4 heterojunction photocatalyst,” Dalton Transactions, vol. 41, no. 12, pp. 3387–3394, 2012. View at Publisher · View at Google Scholar · View at Scopus
  24. C. Pan and Y. Zhu, “Size-controlled synthesis of BiPO4 nanocrystals for enhanced photocatalytic performance,” Journal of Materials Chemistry, vol. 21, no. 12, pp. 4235–4241, 2011. View at Publisher · View at Google Scholar · View at Scopus
  25. M. Niu, F. Huang, L. Cui, P. Huang, Y. Yu, and Y. Wang, “Hydrothermal synthesis, structural characteristics, and enhanced photocatalysis of SnO2/α-Fe2O3 semiconductor nanoheterostructures,” ACS Nano, vol. 4, no. 2, pp. 681–688, 2010. View at Publisher · View at Google Scholar · View at Scopus
  26. S. Zhang, C. Zhang, Y. Man, and Y. Zhu, “Visible-light-driven photocatalyst of Bi2WO6 nanoparticles prepared via amorphous complex precursor and photocatalytic properties,” Journal of Solid State Chemistry, vol. 179, no. 1, pp. 62–69, 2006. View at Publisher · View at Google Scholar · View at Scopus
  27. X. Wang, S. Li, H. Yu, and J. Yu, “In situ anion-exchange synthesis and photocatalytic activity of Ag8W4O16/AgCl-nanoparticle core-shell nanorods,” Journal of Molecular Catalysis A, vol. 334, no. 1-2, pp. 52–59, 2011. View at Publisher · View at Google Scholar · View at Scopus
  28. J. Shi, “On the synergetic catalytic effect in heterogeneous nanocomposite catalysts,” Chemical Reviews, vol. 113, no. 3, pp. 2139–2181, 2013. View at Publisher · View at Google Scholar
  29. F. T. Li, Y. Zhao, Y. J. Hao et al., “N-doped P25 TiO2-amorphous Al2O3 composites: one-step solution combustion preparation and enhanced visible-light photocatalytic activity,” Journal of Hazardous Materials, vol. 239-240, pp. 118–127, 2012. View at Publisher · View at Google Scholar
  30. J. X. Wang, S. S. Xie, H. J. Yuan et al., “Synthesis, structure, and photoluminescence of Zn2SnO4 single-crystal nanobelts and nanorings,” Solid State Communications, vol. 131, no. 7, pp. 435–440, 2004. View at Publisher · View at Google Scholar · View at Scopus
  31. X. Liu, J. Wang, E. Liang, and W. Zhang, “Enhancing mechanism of visible-light absorption for photovoltaic response and photoluminescence of Zn2SnO4 with high solubility of Bi3+,” Applied Surface Science, vol. 280, pp. 556–563, 2013. View at Publisher · View at Google Scholar
  32. Y. Ohko, A. Fujishima, and K. Hashimoto, “Kinetic analysis of the photocatalytic degradation of gas-phase 2-propanol under mass transport-limited conditions with a TiO2 film photocatalyst,” Journal of Physical Chemistry B, vol. 102, no. 10, pp. 1724–1729, 1998. View at Google Scholar · View at Scopus
  33. L. Cao, F. J. Spiess, A. Huang et al., “Heterogeneous photocatalytic oxidation of 1-butene on SnO2 and TiO2 films,” Journal of Physical Chemistry B, vol. 103, no. 15, pp. 2912–2917, 1999. View at Google Scholar · View at Scopus
  34. X. Song and L. Gao, “Fabrication of hollow hybrid microspheres coated with silica/titania via sol-gel process and enhanced photocatalytic activities,” Journal of Physical Chemistry C, vol. 111, no. 23, pp. 8180–8187, 2007. View at Publisher · View at Google Scholar · View at Scopus