Electrochemical Coprecipitation of Zinc and Aluminum in Aqueous Electrolytes for ZnO and AZO Coverage Deposition
Table 2
Characteristics of ZnO:Al coatings after annealing at 530°C for 1 hours. 1 μm thick films have been applied for LAES, EDX, and XPS analyses.
| | Electrolytes | Zn (LAES), at% | Al (LAES), at% | Al/Zn (LAES) | Zn (EDX), at% | Al (EDX), at% | Al/Zn (EDX) | Zn (XPS), at% | Al (XPS), at% | Al/Zn (XPS) |
| | Al-0 | | 0 | | | | | 34.5 | 0 | 0 | | Al-1 | 90.9 | 9.07 | 0.10 | 3.03 | 1.60 | 0.53 | 21.0 | 5.0 | 0.24 | | Al-2 | 86.0 | 14.0 | 0.16 | 2.97 | 5.59 | 1.88 | 7.5 | 15.0 | 2.00 | | Al-4 | 86.3 | 13.7 | 0.16 | 0.88 | 1.58 | 1.80 | 9.7 | 7.2 | 0.74 | | Al-6 | 86.0 | 14.0 | 0.16 | 1.63 | 9.26 | 5.68 | 1.3 | 18.1 | 13.90 | | Al-10 | 84.3 | 15.7 | 0.19 | 3.82 | 16.13 | 4.22 | 23.6 | 18.9 | 23.60 |
|
|