Corrosion Reason Analysis of 13Cr110 Tubing in an Injection and Production Well of the Suqiao Gas Storage Group
Table 2
Metallographic analysis results of tubing samples.
| Samples | Nonmetallic inclusion | Metallurgical structure | Grain size | A | B | C | D | Thin | Thick | Thin | Thick | Thin | Thick | Thin | Thick |
| 84# | 0.5 | 0 | 0.5 | 0 | 0 | 0 | 0.5 | 0 | Tempered martensite | Level 9.0 | 258# | 0.5 | 0 | 0.5 | 0 | 0 | 0 | 0.5 | 0 | Tempered martensite | Level 9.0 | 259# | 0.5 | 0 | 0.5 | 0 | 0 | 0 | 0.5 | 0 | Tempered martensite | Level 9.0 | 364# | 0.5 | 0 | 0.5 | 0 | 0 | 0 | 0.5 | 0 | Tempered martensite | Level 9.0 |
|
|