Corrosion Reason Analysis of 13Cr110 Tubing in an Injection and Production Well of the Suqiao Gas Storage Group
Table 7
Composition analysis results of corrosion products at different positions of 258# sample surface.
| Number | C | O | Mg | Al | Si | K | S | Ca | Cr | Mn | Fe | Ni | Cu | Total |
| 1 | Weight% | 13.48 | 35.04 | | 0.28 | 0.51 | 0.52 | 0.90 | 1.35 | 24.41 | | 20.46 | 2.35 | 0.70 | 100.00 | Atomic% | 26.08 | 50.90 | | 0.24 | 0.42 | 0.31 | 0.66 | 0.78 | 10.91 | | 8.51 | 0.93 | 0.26 | | 2 | Weight% | 8.17 | 37.58 | | 0.40 | 0.73 | | 0.34 | 0.72 | 4.76 | 0.48 | 44.92 | 1.91 | | 100.00 | Atomic% | 16.86 | 58.20 | | 0.36 | 0.64 | | 0.26 | 0.45 | 2.27 | 0.21 | 19.93 | 0.81 | | | 3 | Weight% | 12.39 | 53.57 | 2.47 | 0.32 | 0.73 | 0.21 | | 22.90 | | | 7.41 | | | 100.00 | Atomic% | 19.72 | 64.04 | 1.94 | 0.23 | 0.50 | 0.10 | | 10.93 | | | 2.54 | | | |
|
|