Corrosion Reason Analysis of 13Cr110 Tubing in an Injection and Production Well of the Suqiao Gas Storage Group
Table 8
Composition analysis results of corrosion products at different positions of 259# sample surface.
| Number | C | O | Mg | Al | Si | K | S | Ca | Cr | Ti | Fe | Ni | Total |
| 1 | Weight% | 9.88 | 34.54 | | | | 1.08 | 1.48 | 1.78 | 31.70 | | 17.07 | 2.46 | 100.00 | Atomic% | 20.28 | 53.21 | | | | 0.68 | 1.14 | 1.09 | 15.03 | | 7.54 | 1.03 | | 2 | Weight% | 7.76 | 39.15 | 0.43 | 0.39 | | | 0.41 | 0.72 | 5.61 | 2.75 | 41.30 | 1.48 | 100.00 | Atomic% | 15.82 | 59.89 | 0.43 | 0.34 | | | 0.31 | 0.44 | 2.64 | 1.40 | 18.10 | 0.62 | | 3 | Weight% | 11.99 | 52.56 | 2.60 | | 0.17 | | 0.20 | 26.82 | | | 5.65 | | 100.00 | Atomic% | 19.30 | 63.50 | 2.07 | | 0.12 | | 0.12 | 12.93 | | | 1.96 | | |
|
|