Effects of Composite Formulation on Mechanical Properties of Biodegradable Poly(Propylene Fumarate)/Bone Fiber Scaffolds
Table 2
Summary of Results for Ultimate Strength and Compressive Modulus.
| | Dry Samples | Wet Samples |
| | Formulation | Modulus (MPa) | Ultimate Strength (MPa) | Modulus (MPa) | Ultimate Strength (MPa) |
| | 1 | 117 ± 39 | 9.9 ± 0.3 | 24.5 ± 4.6 | 3.3 ± 0.4 | | 2 | 108 ± 15 | 13.2 ± 14 | 66.0 ± 7.7 | 7.0 ± 0.7 | | 3 | 246 ± 1.0 | 11.1 ± 0.6 | 358 ± 5.2 | 16.6 ± 4.4 | | 4 | 271 ± 29 | 20.3 ± 8.0 | 184 ± 1.3 | 12.0 ± 0.5 | | 5 | 258 ± 25 | 13.3 ± 1.0 | 157 ± 22 | 8.7 ± 2.1 | | 6 | 184 ± 0.5 | 13.0 ± 0.5 | 101 ± 0.2 | 9.2 ± 0.6 | | 7 | 21.3 ± 5.7 | 2.1 ± 0.9 | 2.8 ± 0.1 | 0.4 ± 0.0 | | 8 | 220 ± 17 | 18.4 ± 4.0 | 157 ± 8.2 | 11.0 ± 2.0 |
|
|
Values are given as means ± standard deviations for .
|