Quantitative Analysis of Semicrystalline Blends SAXS Data: Theoretical Modeling versus Linear Correlation Function

Figure 1

Best fit between theoretical 𝐼₁(𝑞) and experimental 𝐼(𝑞) SAXS intensity profiles for (a) pure PVDF; (b) 90 wt% PVDF sample; (c) 80 wt% PVDF sample; (d) 70 wt% PVDF sample; (e) 60 wt% PVDF sample; (f) 50 wt% PVDF sample.