Correlation of Polymerization Conditions with Thermal and Mechanical Properties of Polyethylenes Made with Ziegler-Natta Catalysts
Table 1
Ethylene polymerization using Ziegler-Natta catalyst.
| S/no. | Polymerization | Results | Catalyst | | | Temp. | Time | Yield | Activity | Mn | Mw | PDI | (mg) | (atm) | (atm) | (°C) | (hour) | (g) | (kg PE/G cat·h) | (kg/mol) | (kg/mol) | Mw/Mn |
| 1 | 3.0 | 5 | 0 | 60 | 0.5 | 9.0 | 8.3 | 88 | 325 | 3.69 | 2 | 3.1 | 5 | 0 | 60 | 1 | 20.1 | 6.5 | 83 | 340 | 4.10 | 3 | 3.4 | 5 | 0 | 80 | 0.5 | 8.3 | 4.9 | 78 | 310 | 3.97 | 4 | 3.4 | 5 | 0 | 80 | 1 | 9.6 | 2.8 | 80 | 317 | 3.96 | 5 | 2.9 | 5 | 2 | 60 | 0.5 | 8.1 | 6.6 | 30 | 111 | 3.70 | 6 | 3.0 | 5 | 2 | 60 | 1 | 17.4 | 5.8 | 25 | 112 | 4.48 | 7 | 3.0 | 5 | 2 | 80 | 0.5 | 4.8 | 3.2 | 19 | 89 | 4.68 | 8 | 3.0 | 5 | 2 | 80 | 1 | 7.8 | 2.6 | 23 | 102 | 4.43 | 9 | 3.0 | 5 | 5 | 60 | 0.5 | 4.9 | 3.3 | 19 | 103 | 5.42 | 10 | 3.0 | 5 | 5 | 60 | 1 | 7.7 | 2.6 | 14 | 92 | 6.57 | 11 | 3.3 | 5 | 5 | 80 | 0.5 | 3.1 | 1.9 | 10 | 57 | 5.70 | 12 | 3.0 | 5 | 5 | 80 | 1 | 3.5 | 1.0 | 12 | 66 | 5.50 | 13 | 3.4 | 10 | 0 | 60 | 0.5 | 38.5 | 22.6 | 167 | 662 | 3.96 | 14 | 3.5 | 10 | 0 | 60 | 1 | 45.8 | 13.1 | 158 | 655 | 4.15 | 15 | 3.3 | 10 | 0 | 80 | 0.5 | 26.5 | 16.1 | 162 | 617 | 3.81 | 16 | 3.1 | 10 | 0 | 80 | 1 | 28.5 | 9.2 | 154 | 625 | 4.06 | 17 | 3.3 | 10 | 2 | 60 | 0.5 | 23.9 | 14.5 | 35 | 176 | 5.03 | 18 | 3.3 | 10 | 2 | 60 | 1 | 43.6 | 13.2 | 30 | 161 | 5.37 | 19 | 3.1 | 10 | 2 | 80 | 0.5 | 22.9 | 14.8 | 25 | 127 | 5.08 | 20 | 3.2 | 10 | 2 | 80 | 1 | 39.1 | 12.2 | 68 | 267 | 3.93 | 21 | 3.0 | 10 | 5 | 60 | 0.5 | 20.2 | 13.5 | 40 | 226 | 5.65 | 22 | 3.2 | 10 | 5 | 60 | 1 | 32.1 | 10.3 | 49 | 239 | 4.88 | 23 | 3.0 | 10 | 5 | 80 | 0.5 | 15.4 | 10.3 | 39 | 169 | 4.33 | 24 | 3.2 | 10 | 5 | 80 | 1 | 25.1 | 7.8 | 41 | 178 | 4.34 |
|
|